35WW300 is a high-grade electrical steel designed for critical applications in the electrical industry. Its composition, primarily iron and silicon with minimal carbon, provides a superior blend of properties:
Magnetic Properties: High magnetic permeability, high saturation induction, low hysteresis loss, and low eddy current loss.
Mechanical Properties: High yield strength, high hardness, and high ductility.
These characteristics make 35WW300 an excellent choice for constructing the cores of motors and transformers, significantly improving their operational efficiency and overall performance.
Specification Parameters
| Standard of Electromagnetic Properties | ||||||
| Grade | Thickness (mm) | Max.Core loss P155 (W/kg) | Min.Magnetic Polarization J5000(T) | Min.Stacking Factor | Min.Number of Bends | Conventional Density (kg/dm) |
| 35WW300 | 0.35 | 2.65 | 1.64 | 0.95 | 2 | 7.65 |
| Typical electromagnetic properties | ||||||||||
| Grade | Thickness (mm) | Conventional Density (kg/dm³) | Specific Total Loss(W/kg) | Magnetic Polarization(T) | ||||||
| P 0/50 | P15/50 | P0/60 | P 5/60 | J000 | J250 | 0 | J0000 | |||
| 35WW300 | 0.35 | 7.65 | 1 | 2.45 | 1.26 | 3.07 | 1.49 | 1.6 | 1.68 | 1.8 |
| Typical mechanical properties | |||||||||||
| Grade | Thickness (mm) | Yield Strength (MPa) | TensileStrength (MPa) | Elongation (%) | Hardness | Number of Bends | Stacking Factor | ||||
| L | C | L | C | L | C | HV5 | L | C | |||
| 35WW300 | 0.35 | 395 | 410 | 510 | 530 | 25 | 26 | 185 | 12 | 10 | 0.98 |