35WW360 is a type of electrical steel known as a soft magnetic material. It is characterized by its high magnetic induction, high strength, and good conductivity, which makes it widely useful in the power, electronics, and communications sectors.
Its excellent properties are achieved through a manufacturing process that includes cold rolling and the application of an insulating coating. The high magnetic induction of 35WW360 allows it to create strong magnetic fields, making it suitable for high-power and high-frequency electronic devices. Additionally, its good thermal conductivity and mechanical strength make it an ideal choice for components in motors and transformers.
Specification Parameters
| Standard of Electromagnetic Properties | ||||||
| Grade | Thickness (mm) | Max.Core loss P155 (W/kg) | Min.Magnetic Polarization J5000(T) | Min.Stacking Factor | Min.Number of Bends | Conventional Density (kg/dm) |
| 35WW360 | 0.35 | 3.2 | 1.65 | 0.95 | 3 | 7.65 |
| Typical electromagnetic properties | ||||||||||
| Grade | Thickness (mm) | Conventional Density (kg/dm³) | Specific Total Loss(W/kg) | Magnetic Polarization(T) | ||||||
| P 0/50 | P15/50 | P0/60 | P 5/60 | J000 | J250 | 0 | J0000 | |||
| 35WW360 | 0.35 | 7.65 | 1.16 | 2.69 | 1.44 | 3.35 | 1.5 | 1.6 | 1.69 | 1.8 |
| Typical mechanical properties | |||||||||||
| Grade | Thickness (mm) | Yield Strength (MPa) | TensileStrength (MPa) | Elongation (%) | Hardness | Number of Bends | Stacking Factor | ||||
| L | C | L | C | L | C | HV5 | L | C | |||
| 35WW360 | 0.35 | 380 | 400 | 490 | 505 | 27 | 29 | 170 | 17 | 16 | 0.98 |