SHANGHAI RUICHAO INDUSTRIAL
SHANGHAI RUICHAO INDUSTRIAL
50WW1300 is a high-performance non-oriented silicon steel coil engineered to deliver exceptional magnetic properties, including high magnetic permeability, low coercivity, and high resistivity. These characteristics make it ideal for advanced power equipment applications, ensuring efficient energy conversion and minimal core losses.
Widely utilized across global industries—such as power generation, electronics, and machinery—this material meets stringent requirements for reliability and efficiency. It is primarily employed in the manufacturing of critical power devices, including motors, transformers, and inductors, where its superior magnetic performance enhances operational stability and energy savings.
Specification Parameters
| Standard of Electromagnetic Properties | ||||||
| Grade | Thickness (mm) | Max.Core loss P155 (W/kg) | Min.Magnetic Polarization J5000(T) | Min.Stacking Factor | Min.Number of Bends | Conventional Density (kg/dm) |
| 50WW1300 | 0.5 | 7 | 1.74 | 0.97 | 10 | 7.85 |
| Typical electromagnetic properties | ||||||||||
| Grade | Thickness (mm) | Conventional Density (kg/dm³) | Specific Total Loss(W/kg) | Magnetic Polarization(T) | ||||||
| P 0/50 | P15/50 | P0/60 | P 5/60 | J000 | J250 | 0 | J0000 | |||
| 50WW1300 | 0.5 | 7.85 | 2.49 | 5.51 | 3.16 | 7.06 | 1.57 | 1.68 | 1.75 | 1.86 |
| Typical mechanical properties | |||||||||||
| Grade | Thickness (mm) | Yield Strength (MPa) | TensileStrength (MPa) | Elongation (%) | Hardness | Number of Bends | Stacking Factor | ||||
| L | C | L | C | L | C | HV5 | L | C | |||
| 50WW1300 | 0.5 | 230 | 240 | 350 | 360 | 50 | 50 | 100 | ≥20 | ≥20 | 0.985 |