Produced primarily by WISCO, 50WW600 is a grade of non-oriented electrical steel. Its nomenclature provides key specifications: the first two digits ("50") indicate a material thickness of 0.5 mm, and the following digits ("600") denote that its maximum core loss is 100 times that number, i.e., 6.00 Watts per kilogram (W/kg) when measured at 1.5 Tesla and 50 Hz.
These properties—low iron loss and good magnetic performance—make it a widely used material in the cores of electrical equipment like motors and transformers, where it helps to improve energy efficiency.
Specification Parameters
| Standard of Electromagnetic Properties | ||||||
| Grade | Thickness (mm) | Max.Core loss P155 (W/kg) | Min.Magnetic Polarization J5000(T) | Min.Stacking Factor | Min.Number of Bends | Conventional Density (kg/dm) |
| 50WW600 | 0.5 | 4.2 | 1.68 | 0.97 | 10 | 7.75 |
| Typical electromagnetic properties | ||||||||||
| Grade | Thickness (mm) | Conventional Density (kg/dm³) | Specific Total Loss(W/kg) | Magnetic Polarization(T) | ||||||
| P 0/50 | P15/50 | P0/60 | P 5/60 | J000 | J250 | 0 | J0000 | |||
| 50WW600 | 0.5 | 7.75 | 1.71 | 3.79 | 2.16 | 4.82 | 1.53 | 1.64 | 1.72 | 1.83 |
| Typical mechanical properties | |||||||||||
| Grade | Thickness (mm) | Yield Strength (MPa) | TensileStrength (MPa) | Elongation (%) | Hardness | Number of Bends | Stacking Factor | ||||
| L | C | L | C | L | C | HV5 | L | C | |||
| 50WW600 | 0.5 | 280 | 295 | 410 | 425 | 40 | 42 | 130 | ≥20 | ≥20 | 0.985 |