B35A360 is a silicon electrical steel (0.8–4.8% silicon content) processed through hot and cold rolling. It delivers low iron loss, high magnetic flux density, and excellent punching performance, with strong adhesion of the insulating film and good weldability. These properties make it ideal for high-efficiency electromagnetic applications.
Specification Parameters
| Standard of electromagnetic properties | ||||||
| Grade | Thickness (mm) | Max.Core loss P55 (W/kg) | Min.Magnetic Polarization J5000 (T) | Min.Stacking Factor | Min.Number of Bends | Conventional Density(kg/dm³) |
| B35A360 | 0.35 | 3.2 | 1.65 | 0.95 | 3 | 7.65 |
| Typical electromagnetic properties | ||||||||||
| Grade | Thickness(mm) | Conventional Density (kg/dm²) | Specific Total Loss(W/kg) | Magnetic Polarization(T) | ||||||
| P1.0/5 | P1.50 | P10/50 | P | J1000 | J2500 | J5000 | J100 | |||
| B35A360 | 0.35 | 7.65 | 1.25 | 2.8 | 1.55 | 3.44 | 1.51 | 1.6 | 1.68 | 1.8 |
| Typical mechanical properties | |||||||||||
| Grade | Thickness(mm) | YieldStrength(MPa) | Tensile Strength(MPa) | Elongation(%) | Hardness | Number of Bends | Stacking Factor | ||||
| L | C | L | C | L | C | HV1 | L | C | |||
| B35A360 | 0.35 | 362 | 375 | 508 | 520 | 29 | 30 | 188 | ≥20 | ≥20 | 0.985 |