B50A1300 is a cost-effective electrical steel designed for industrial applications requiring reliable performance without premium efficiency. With a thickness of 0.50mm, it offers moderate magnetic properties and functional iron loss characteristics, making it suitable for medium-duty motors, transformers, and generators. Its ease of punching, stacking, and processing reduces manufacturing complexity and cost, providing a practical solution for projects where operational durability and budget efficiency are prioritized over high-end energy savings.
Specification Parameters
| Standard of electromagnetic properties | ||||||
| Grade | Thickness (mm) | Max.Core loss P55 (W/kg) | Min.Magnetic Polarization J5000 (T) | Min.Stacking Factor | Min.Number of Bends | Conventional Density(kg/dm³) |
| B50A1300 | 0.5 | 7 | 1.74 | 0.97 | 10 | 7.85 |
| Typical electromagnetic properties | ||||||||||
| Grade | Thickness(mm) | Conventional Density (kg/dm²) | Specific Total Loss(W/kg) | Magnetic Polarization(T) | ||||||
| P1.0/5 | P1.50 | P10/50 | P | J1000 | J2500 | J5000 | J100 | |||
| B50A1300 | 0.5 | 7.85 | 2.84 | 5.98 | 3.59 | 7.52 | 1.59 | 1.68 | 1.76 | 1.87 |
| Typical mechanical properties | |||||||||||
| Grade | Thickness(mm) | YieldStrength(MPa) | Tensile Strength(MPa) | Elongation(%) | Hardness | Number of Bends | Stacking Factor | ||||
| L | C | L | C | L | C | HV1 | L | C | |||
| B50A1300 | 0.5 | 239 | 247 | 352 | 360 | 41 | 41 | 108 | ≥20 | ≥20 | 0.99 |